Uniaxial drawing behaviour of poly(trimethylene terephthalate)

Abstract

In this thesis, the uniaxial drawing behaviour of poly (trimethylene terephthalate) (PTT) was studied. PTT is a new commercial polyester, which has a similar molecular structure to the well-known PET. 37% of the PTT polymer can be manufactured using renewable sourced material. The drawing behaviour of PTT was studied using different stretching conditions above glass transition temperature and then compared to the drawing behaviour of PET. The development of orientation was measured using a Metricon Prism Coupler and the development of crystallization was determined using Different scanning calorimetry (DSC), density measurements, thermal shrinkage and Wide angle X-ray scattering (WAXS).

AB3:Tämän diplomityön tarkoituksena oli tutkia Poly-trimetyleeni-teraftalaatin (PTT) yhdensuuntaisen vedon käyttäytymistä. PTT on viime aikoina tullut mandolliseksi valmistaa kaupallisessa mittakaavassa. PTT:n molekyylirakenne on lähellä PET:n molekyylirakennetta. PET on tunnettu polymeeri muovikalvoteollisuudessa. 37% PTT:n lähtöaineista voidaan valmistaa uusiutuvasta luonnonvarasta, maissista. PTT:n käyttäytymistä vedossa tutkittiin erilaisissa veto-olosuhteissa lasisiirtymälämpötilan yläpuolella. Saatuja tuloksia verrattiin PET muovikalvon käyttäytymiseen. Diplomityön päätavoite oli orientoitumisen ja kiteytymisen kehittyminen vedon aikana. Orientoituminen määritettiin Metriconilla, joka mittaa valontaitekerrointa. Kiteytymistä arvioitiin käyttämällä useampaa menetelmää: DSC, tiheys, lämpötila kutistuminen, DSC ja WAXS (laajan kulman röntgendiffraktio).